TheGreatWukong [2017-06-16 00:28:36 +0000 UTC]
NICE
very curious of your shaping and beveling process
π: 0 β©: 1
Dragon8or In reply to TheGreatWukong [2018-07-10 15:35:51 +0000 UTC]
Done by eye with an angle grinder, then shaped with a chisel and polished with wet and dry.
π: 0 β©: 0
TheDraconian [2014-09-14 13:35:41 +0000 UTC]
I wish I had a sword laying around in myΒ garage, but I don't. Mainly because I don't have a garage.Β
π: 0 β©: 1
Dragon8or In reply to TheDraconian [2014-09-15 10:23:39 +0000 UTC]
A lounge room is a good place to store them too ^
π: 0 β©: 0
JWright-3D-Graphics [2013-01-13 21:26:18 +0000 UTC]
wow o_0
that looks incredable great work on the blade shame it had to go to waste though
i think ill make a 3d model of this blade and add a handle and guard to to it see what is would have been liked finished
ill send u a link once its done
π: 0 β©: 2
Armameteus [2012-11-06 22:03:19 +0000 UTC]
I'm a sucker for fancifully-designed swords. I'm really liking the shape of the blade; brutal, yet elegant. If you could get it polished back up, tempered and add a proper hilt with an equally fancy cross-guard or something, this would be one snazzy piece of work.
π: 0 β©: 1
loveshina [2012-04-30 06:50:05 +0000 UTC]
You ought to temper it yourself, its a very beautiful sword.
π: 0 β©: 1
loveshina In reply to Dragon8or [2012-05-01 00:15:07 +0000 UTC]
Ah, that's a shame.
π: 0 β©: 0
Dreadcross [2012-04-30 06:27:31 +0000 UTC]
Very nice. It actually looks like a sword you would use in combat.
π: 0 β©: 1
Dreadcross In reply to Dragon8or [2012-05-02 07:08:04 +0000 UTC]
Good luck with that.
π: 0 β©: 1
THEloathedONE [2012-04-29 14:13:34 +0000 UTC]
why not temper it yourself?
π: 0 β©: 1
Dragon8or In reply to THEloathedONE [2012-04-30 21:52:52 +0000 UTC]
Sadly I dont have the means to do it where i live at the moment.
π: 0 β©: 1
THEloathedONE In reply to Dragon8or [2012-05-01 04:37:05 +0000 UTC]
i am just getting into blacksmithing, have a forge and a 4ft railroad track, going to build a tempering box next
π: 0 β©: 1